@MastersThesis{Contin:2014:DeDiCV,
               author = "Contin, Andr{\'e}",
                title = "Deposi{\c{c}}{\~a}o de diamante CVD sobre a{\c{c}}o 304 com 
                         interface de sic obtida por laser cladding",
               school = "Instituto Nacional de Pesquisas Espaciais (INPE)",
                 year = "2014",
              address = "S{\~a}o Jos{\'e} dos Campos",
                month = "2014-02-26",
             keywords = "filme de diamante CVD, laser cladding, A{\c{c}}o inox 304, HFCVD, 
                         barreira intermedi{\'a}ria, CVD diamond film, laser cladding. 3. 
                         304 stainless steel, HFCVD, intermediate barrier.",
             abstract = "O emprego de filmes de diamante CVD em substratos de a{\c{c}}o 
                         {\'e} uma aplica{\c{c}}{\~a}o de grande interesse devido 
                         {\`a}s suas propriedades {\'{\i}}mpares. O uso do diamante CVD 
                         como filme protetor, gera um aumento da dureza superficial, da 
                         condutividade t{\'e}rmica e na redu{\c{c}}{\~a}o do atrito, e 
                         consequentemente, melhor prote{\c{c}}{\~a}o {\`a} 
                         corros{\~a}o. Apesar das dificuldades ainda encontradas em termos 
                         de ader{\^e}ncia entre filmes de diamante e substratos de 
                         a{\c{c}}o, a baixa raz{\~a}o custo-benef{\'{\i}}cio do 
                         recobrimento com diamante sint{\'e}tico {\'e} vantajosa e, 
                         portanto, almejada. O objetivo deste trabalho foi o de depositar 
                         filmes de diamante CVD aderentes em substratos de a{\c{c}}o inox 
                         304, utilizando uma nova t{\'e}cnica de forma{\c{c}}{\~a}o de 
                         barreira intermedi{\'a}ria, realizada pelo processo de laser 
                         cladding. Nesta t{\'e}cnica, uma fina camada de p{\'o} {\'e} 
                         irradiada e fundida por um feixe de laser com o prop{\'o}sito de 
                         fundir a camada de p{\'o} e a camada superficial do substrato 
                         para criar o recobrimento. O controle dos par{\^a}metros do feixe 
                         do laser permite a cria{\c{c}}{\~a}o de camadas homog{\^e}neas 
                         de recobrimento, em {\'a}reas relativamente grandes, em poucos 
                         segundos. Neste trabalho, utilizou-se o p{\'o} de carbeto de 
                         sil{\'{\i}}cio (SiC) para criar a camada intermedi{\'a}ria. 
                         Antes do crescimento de diamante, as amostras foram submetidas ao 
                         processo de semeadura com p{\'o} de diamante. A 
                         deposi{\c{c}}{\~a}o dos filmes de diamante foi realizada em um 
                         reator HFCVD (Hot Filament Chemical Vapor Deposition) com 
                         diferentes concentra{\c{c}}{\~o}es de gases para filmes 
                         microcristalinos e nanocristalinos. Como parte dos resultados 
                         obtidos, o teste de indenta{\c{c}}{\~a}o Rockwell mostrou a 
                         melhoria da ades{\~a}o dos filmes de diamante nos substratos. A 
                         microscopia eletr{\^o}nica de varredura (MEV) revelou a 
                         morfologia dos filmes de diamante. Por difra{\c{c}}{\~a}o de 
                         raios-X foi identificada as fases cristalinas da camada de SiC. O 
                         n{\'{\i}}vel de tens{\~a}o residual dos filmes de diamante e o 
                         de ader{\^e}ncia da camada de SiC foram avaliados pela 
                         espectroscopia Raman e ensaio de microscratch, respectivamente. 
                         ABSTRACT: The use of CVD diamond films on steel substrates is an 
                         application of great interest due to their unique properties. The 
                         use of CVD diamond film as a protective film generates an increase 
                         in surface hardness, thermal conductivity and reduced friction 
                         and, consequently, better corrosion protection. Despite the 
                         difficulties still encountered in terms of adhesion between 
                         diamond films and steel substrates, low cost-benefit ratio of the 
                         coating with synthetic diamond is advantageous and, therefore, 
                         desired. The objective of this work was to deposit CVD diamond 
                         films adherents in 304 stainless steel substrates using a new 
                         technique of forming intermediate barrier, made by laser cladding 
                         process. In this technique, a thin layer of powder is irradiated 
                         and melted by a laser beam in order to melt the powder layer and 
                         the surface layer of the substrate to create the coating. The 
                         parameters control of the laser beam allows the creation of 
                         homogeneous layers of coating, in relatively large areas in 
                         seconds. In this work, we used the powdered silicon carbide (SiC) 
                         to create an intermediate layer. Before the diamond growth, the 
                         samples were subjected to the process of seeding with diamond 
                         dust. The deposition of diamond films was carried out in a reactor 
                         HFCVD (Hot Filament Chemical Vapor Deposition) with different 
                         concentrations of gases for microcrystalline and nanocrystalline 
                         films. As part of the results obtained, the Rockwell indentation 
                         test showed the improvement of adhesion of diamond films on 
                         substrates. The scanning electron microscopy (SEM) revealed the 
                         morphology of the diamond films. The X-ray diffraction identified 
                         the crystalline phases of the SiC layer. The level of residual 
                         stress of the diamond films and the adhesion of the SiC layer were 
                         evaluated by Raman spectroscopy and microscratch test, 
                         respectively.",
            committee = "Corat, Evaldo Jos{\'e} (presidente/orientador) and Vasconcelos, 
                         Get{\'u}lio de (orientador) and Gavinier, Divani Barbosa and 
                         Bonetti, Luis Francisco",
         englishtitle = "CVD diamond deposition on steel 304 with sic interface by laser 
                         cladding",
             language = "pt",
                pages = "96",