| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21b.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34P/3LKJF4B | |||
| Repositório | sid.inpe.br/mtc-m21b/2016/05.03.17.03 (acesso restrito) | |||
| Última Atualização | 2016:05.03.17.05.11 (UTC) administrator | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2016/05.03.17.03.52 | |||
| Última Atualização dos Metadados | 2018:06.04.02.40.46 (UTC) administrator | |||
| DOI | 10.1016/j.jdent.2016.03.004 | |||
| ISSN | 0300-5712 1879-176X | |||
| Chave de Citação | CamposRaMaBoSoMe:2016:NeSiYT | |||
| Título | A new silica-infiltrated Y-TZP obtained by the sol-gel method  | |||
| Ano | 2016 | |||
| Mês | May | |||
| Data de Acesso | 16 jun. 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 3151 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Campos, T. M. B. 2 Ramos, N. C. 3 Machado, João Paulo Barros 4 Bottino, M. A. 5 Souza, R. O. A. 6 Melo, R. M. | |||
| Identificador de Curriculo | 1 2 3 8JMKD3MGP5W/3C9JHER | |||
| Grupo | 1 2 3 LAS-CTE-INPE-MCTI-GOV-BR | |||
| Afiliação | 1 Instituto Tecnológico de Aeronáutica (ITA) 2 Universidade Estadual Paulista (UNESP) 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Universidade Estadual Paulista (UNESP) 5 Universidade Federal do Rio Grande do Norte (UFRN) 6 Universidade Estadual Paulista (UNESP) | |||
| Endereço de e-Mail do Autor | 1 2 3 joao.machado@inpe.br 4 5 6 renata.marinho@ict.unesp.br | |||
| Revista | Journal of Dentistry | |||
| Volume | 48 | |||
| Páginas | 55-61 | |||
| Nota Secundária | A1_ODONTOLOGIA A1_ENGENHARIAS_III A2_SAÚDE_COLETIVA A2_MEDICINA_II A2_MEDICINA_I A2_INTERDISCIPLINAR A2_ENGENHARIAS_IV A2_ENGENHARIAS_II A2_ENGENHARIAS_I B1_QUÍMICA B1_MATERIAIS B1_CIÊNCIAS_BIOLÓGICAS_III B1_CIÊNCIAS_BIOLÓGICAS_II B1_CIÊNCIAS_BIOLÓGICAS_I B1_BIOTECNOLOGIA B2_ASTRONOMIA_/_FÍSICA | |||
| Histórico (UTC) | 2016-05-03 17:03:52 :: simone -> administrator :: 2018-06-04 02:40:46 :: administrator -> simone :: 2016 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | Bond strength Flexural strength Silica Sol-gel Weibull Zirconia | |||
| Resumo | Objective The aim of this study was to evaluate silica infiltration into dental zirconia (VITA In-Ceram 2000 YZ, Vita Zahnfabrik) and its effects on zirconia's surface characteristics, structural homogeneity and bonding to a resin cement. Methods Infiltration was performed by immersion of the pre-sintered zirconia specimens in silica sols for five days (ZIn). Negative (pure zirconia specimens, ZCon-) and positive controls (specimens kept in water for 5 days, ZCon+) were also performed. After sintering, the groups were evaluated by X-ray diffraction (XRD), grazing angle X-ray diffraction (DRXR), scanning electron microscopy (SEM), contact angle measurements, optical profilometry, biaxial flexural test and shear bonding test. Weibull analysis was used to determine the Weibull modulus (m) and characteristic strength (σ0) of all groups. Results There were no major changes in strength for the infiltrated group, and homogeneity (m) was also increased. A layer of ZrSiO4 was formed on the surface. The bond strength to resin cement was improved after zirconia infiltration, acid conditioning and the use of an MDP primer. Conclusion The sol-gel method is an efficient and simple method to increase the homogeneity of zirconia. Infiltration also improved bonding to resin cement. Clinical significance The performance of a zirconia infiltrated by silica gel improved in at least two ways: structural homogeneity and bonding to resin cement. The infiltration is simple to perform and can be easily managed in a prosthesis laboratory. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > A new silica-infiltrated... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | campos_anew.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Repositório Espelho | urlib.net/www/2011/03.29.20.55 | |||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 5 sid.inpe.br/mtc-m21/2012/07.13.14.50.56 1 | |||
| Divulgação | WEBSCI; PORTALCAPES; SCOPUS. | |||
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||