1. Identificação | |
Tipo de Referência | Artigo em Revista Científica (Journal Article) |
Site | mtc-m21d.sid.inpe.br |
Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
Identificador | 8JMKD3MGP3W34T/48E7Q4P |
Repositório | sid.inpe.br/mtc-m21d/2023/01.25.15.44 (acesso restrito) |
Última Atualização | 2023:01.25.15.44.04 (UTC) simone |
Repositório de Metadados | sid.inpe.br/mtc-m21d/2023/01.25.15.44.04 |
Última Atualização dos Metadados | 2023:02.17.15.54.19 (UTC) administrator |
DOI | 10.34172/joddd.2022.029 |
Chave de Citação | FigueiredoSMSQMPN:2022:EfNaZi |
Título | Effect of the nanofilm-coated zirconia ceramic on resin cement bond strength |
Ano | 2022 |
Data de Acesso | 02 jun. 2024 |
Tipo de Trabalho | journal article |
Número de Arquivos | 1 |
Tamanho | 1028 KiB |
|
2. Contextualização | |
Autor | 1 Figueiredo, Viviane Maria Gonçalves de 2 Silva, Alecsandro de Moura 3 Massi, marcos 4 Silva Sobrinho, Argemiro Soares da 5 Queiroz, José Renato Cavalcanti de 6 Machado, João Paulo Barros 7 Prado, Renata Falchete do 8 Nogueira Júnior, Lafayette |
Identificador de Curriculo | 1 2 3 4 5 6 8JMKD3MGP5W/3C9JHER |
ORCID | 1 0000-0003-4657-0984 2 3 4 5 6 7 0000-0001-5970-0464 |
Grupo | 1 2 3 4 5 6 COPDT-CGIP-INPE-MCTI-GOV-BR |
Afiliação | 1 Universidade Estadual Paulista (UNESP) 2 Universidade Estadual Paulista (UNESP) 3 Instituto Tecnológico de Aeronáutica (ITA) 4 Instituto Tecnológico de Aeronáutica (ITA) 5 Laureate University 6 Instituto Nacional de Pesquisas Espaciais (INPE) 7 Universidade Estadual Paulista (UNESP) 8 Universidade Estadual Paulista (UNESP) |
Endereço de e-Mail do Autor | 1 2 3 4 5 6 joao.machado@inpe.br 7 renatafalchete@hotmail.com |
Revista | Journal of Dental Research, Dental Clinics, Dental Prospects |
Volume | 16 |
Número | 3 |
Páginas | 170-178 |
Histórico (UTC) | 2023-01-25 15:45:13 :: simone -> administrator :: 2022 2023-02-17 15:54:19 :: administrator -> simone :: 2022 |
|
3. Conteúdo e estrutura | |
É a matriz ou uma cópia? | é a matriz |
Estágio do Conteúdo | concluido |
Transferível | 1 |
Tipo do Conteúdo | External Contribution |
Tipo de Versão | publisher |
Palavras-Chave | Bonding Fluorine Nanofilm Shear Test Silicon Zirconia |
Resumo | Background. New surface treatments have been proposed to expand the clinical indications of zirconia prostheses. This study aimed to evaluate the effect of silica and fluorine nanofilms on zirconia ceramic on the resin cement bond strength. Methods. Zirconia blocks and discs underwent different surface treatments: untreated zirconia (CON), sandblasted, silica-coated alumina particles (30 µm) (SC), silica nanofilm (SN), and fluorine nanofilm (FN). Nanofilm deposition was performed through plasma enhanced chemical vapor deposition (PECVD). Zirconia surfaces were characterized on disks by morphology (atomic force microscopy, AFM), chemical analysis (x-ray photoelectron spectroscopy, XPS), and contact angle analysis. A silane coupling agent was applied on each treated surface, and a cylinder of resin cement was built up. Half of the specimens in each group were submitted to 6000 thermal cycles (TC). Bond strength was analyzed using the shear test, and the fractographic analysis was performed with stereomicroscopy and SEM/EDS. Statistical analysis was performed through one-way ANOVA and Tukey test in the non-aged and aged specimens. Results. Nanofilms modified the zirconia surface, which became more hydrophilic and chemically reactive. Chemical bonding between Si-O was found in SN, and FN promoted a fluorination process on the ceramic surface, converting zirconia into zirconium oxyfluoride. Specimens of the SN (TC) group failed on pre-testing. FN (TC) bond strength (3.8 MPa) was lower than SC (TC) and CON (TC) after shearing. Adhesive failure predominated in the experimental groups. Silica nanofilm failure occurred after aging. Conclusion. Silica and fluorine nanofilms deposited by PECVD did not promote effective bonding between zirconia and resin cement. |
Área | FISMAT |
Arranjo | urlib.net > BDMCI > Fonds > Produção a partir de 2021 > CGIP > Effect of the... |
Conteúdo da Pasta doc | acessar |
Conteúdo da Pasta source | não têm arquivos |
Conteúdo da Pasta agreement | |
|
4. Condições de acesso e uso | |
Idioma | en |
Arquivo Alvo | joddd-16-170.pdf |
Grupo de Usuários | simone |
Grupo de Leitores | administrator simone |
Visibilidade | shown |
Permissão de Leitura | deny from all and allow from 150.163 |
Permissão de Atualização | não transferida |
|
5. Fontes relacionadas | |
Repositório Espelho | urlib.net/www/2021/06.04.03.40.25 |
Unidades Imediatamente Superiores | 8JMKD3MGPCW/46KUES5 |
Lista de Itens Citando | sid.inpe.br/bibdigital/2022/04.03.23.11 2 sid.inpe.br/mtc-m21/2012/07.13.14.50.56 1 |
Acervo Hospedeiro | urlib.net/www/2021/06.04.03.40 |
|
6. Notas | |
Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel dissemination e-mailaddress format isbn issn label lineage mark month nextedition notes parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey secondarymark secondarytype session shorttitle sponsor subject tertiarymark tertiarytype url |
|
7. Controle da descrição | |
e-Mail (login) | simone |
atualizar | |
|