| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | plutao.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 8JMKD3MGP3W/4AC8ED8 |
| Repositório | sid.inpe.br/plutao/2023/12.11.15.36.33 (acesso restrito) |
| Última Atualização | 2023:12.13.18.04.24 (UTC) lattes |
| Repositório de Metadados | sid.inpe.br/plutao/2023/12.11.15.36.34 |
| Última Atualização dos Metadados | 2024:01.02.17.00.36 (UTC) administrator |
| DOI | 10.1007/s11665-023-08603-z |
| ISSN | 1059-9495 |
| Rótulo | lattes: 7698697775899601 5 OliveiraNFCOMBV:2023:InShPe |
| Chave de Citação | OliveiraNFCOMBV:2023:InShPe |
| Título | Influence of Plasma Immersion Ion Implantation on Ti-6Al-4V Alloy Tensile-Tensile Fatigue Behavior: The Introduction of Shot Peening as a Pretreatment  |
| Ano | 2023 |
| Data de Acesso | 21 jun. 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 3593 KiB |
| 2. Contextualização | |
| Autor | 1 Oliveira, Veronica M. C. A. 2 Nozaki, L. 3 Fernandes, M. F. 4 Cioffi, M. O. H. 5 Oliveira, Rogério de Moraes 6 Martinez, L. G. 7 Barboza, M. J. R. 8 Voorwald, H. J. C. |
| Identificador de Curriculo | 1 2 3 4 5 8JMKD3MGP5W/3C9JJ6L |
| Grupo | 1 2 3 4 5 COPDT-CGIP-INPE-MCTI-GOV-BR |
| Afiliação | 1 Universidade Estadual Paulista (UNESP) 2 Universidade Estadual Paulista (UNESP) 3 Universidade Estadual Paulista (UNESP) 4 Universidade Estadual Paulista (UNESP) 5 Instituto Nacional de Pesquisas Espaciais (INPE) 6 Instituto de Pesquisas Energéticas e Nucleare (IPEN) 7 Universidade de São Paulo (USP) 8 Universidade Estadual Paulista (UNESP) |
| Endereço de e-Mail do Autor | 1 icamcaoliveira@gmail.com 2 3 4 5 rogeirio.oliveira@inpe.br |
| Revista | Journal of Materials Engineering And Performance |
| Volume | 1 |
| Páginas | 100 |
| Nota Secundária | B1_MATERIAIS B1_ENGENHARIAS_IV B1_ENGENHARIAS_III B2_ODONTOLOGIA B2_ENGENHARIAS_II B2_CIÊNCIA_DA_COMPUTAÇÃO B4_QUÍMICA |
| Histórico (UTC) | 2023-12-11 15:36:34 :: lattes -> administrator :: 2023-12-13 18:02:16 :: administrator -> lattes :: 2023 2023-12-13 18:04:29 :: lattes -> administrator :: 2023 2024-01-02 17:00:36 :: administrator -> simone :: 2023 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | fatigue plasma immersion ion implantation residual stress shot peening Ti-6Al-4V alloy |
| Resumo | The purpose of this study was to investigate the influence of combined plasma immersion ion implantation (PIII) and shot peening (SP) treatments on the axial fatigue strength of the Ti-6Al-4V alloy. The specimens were superficially treated with SP and PIII separately and in a combined way. The tensiletensile fatigue behavior was investigated based on microstructural analysis, residual stress measurements, profilometry, Vickers microhardness, scanning electron microscopy, and transmission electron microscopy. Axial fatigue tests at room temperature were performed for the Ti-6Al-4V base material, PIII at 500 and 800 C, SP process and the combination of both surface treatments. The residual stress measurements indicated that PIII treatment at 500 C induced tensile residual stresses of 189 MPa on the material surface. The PIII treatment at 500 C maintained the fatigue resistance of the Ti-6Al-4V alloy in the low-cycle fatigue region, while the PIII treatment at 800 C reduced the fatigue life at all stress levels, from 32 to 96% reduction in lifetime. The combination of SP pretreatment and PIII treatment at 500 C decreased the tensile residual stress value at the surface from 189 to 23 MPa, resulting in an improvement of the fatigue strength compared to only PIII treatment, for N = 106 , the fatigue strength doubled in value. The analysis and tests presented in this work showed the potential of combining PIII and SP treatments to promote the surface protection without the substantial fatigue strength loss frequently associated to surface treatments. |
| Área | FISPLASMA |
| Arranjo | urlib.net > BDMCI > Fonds > Produção a partir de 2021 > CGIP > Influence of Plasma... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Arquivo Alvo | s11665-023-08603-z.pdf |
| Grupo de Usuários | lattes |
| Grupo de Leitores | administrator lattes |
| Visibilidade | shown |
| Política de Arquivamento | denypublisher denyfinaldraft |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/46KUES5 |
| Lista de Itens Citando | sid.inpe.br/mtc-m21/2012/07.13.14.59.24 2 sid.inpe.br/bibdigital/2022/04.03.23.11 1 |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX. |
| Acervo Hospedeiro | dpi.inpe.br/plutao@80/2008/08.19.15.01 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn lineage mark mirrorrepository month nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | simone |
| atualizar | |