@InProceedings{PianassolaCoraAntu:2013:DeEsCo,
author = "Pianassola, Matheus and Corat, Evaldo Jos{\'e} and Antunes, Erica
Freire",
affiliation = "{Universidade Federal de S{\~a}o Paulo (UNIFESP)} and {Instituto
Nacional de Pesquisas Espaciais (INPE)} and {Instituto Nacional de
Pesquisas Espaciais (INPE)}",
title = "Desenvolvimento de estruturas comp{\'o}sitas a base de ep{\'o}xi
e fibra de carbono com deposi{\c{c}}{\~a}o de nanotubos de
carbono",
booktitle = "Anais...",
year = "2013",
organization = "Semin{\'a}rio de Inicia{\c{c}}{\~a}o Cient{\'{\i}}fica do
INPE (SICINPE).",
publisher = "INPE",
address = "S{\~a}o Jos{\'e} dos Campos",
note = "{Bolsa PIBIC/INPE/CNPq}",
keywords = "estruturas comp{\'o}sitas, ep{\'o}xi, fibra de carbono,
nanotubos de carbono.",
abstract = "Este documento relata sobre um procedimento para a
obten{\c{c}}{\~a}o de nanopart{\'{\i}}culas de {\'o}xido de
zinco por eletrodeposi{\c{c}}{\~a}o utilizando uma
solu{\c{c}}{\~a}o aquosa de nitrato de zinco. O eletrodo de
trabalho era feito de filmes de nanotubos de carbono
funcionalizados a plasma de oxig{\^e}nio, verticalmente alinhados
crescidos em Ti num reator de plasma de microondas. A morfologia e
a estrutura cristalina do material foram avaliadas por microscopia
eletr{\^o}nica de varredura e por difra{\c{c}}{\~a}o de
raios-X, respectivamente. As amostras apresentaram difratogramas
contendo picos relacionados tanto com o {\'o}xido de zinco e de
hidroxinitrato de zinco. A fase de hidroxinitrato de zinco foi
transformada em {\'o}xido de zinco apenas por tratamento
t{\'e}rmico a temperaturas ligeiramente maior que 200oC. As
diferen{\c{c}}as na morfologia das nanopart{\'{\i}}culas
(nanofolhas ou esferulitas) foram observadas variando o potencial
de eletrodeposi{\c{c}}{\~a}o ou usando (ou n{\~a}o) de
agita{\c{c}}{\~a}o magn{\'e}tica. ABSTRACT: This document
reports about a procedure for obtaining Zinc Oxide nanoparticles
by electrodeposition using an aqueous solution of zinc nitrate .
The work electrode was made of oxygen-functionalized
vertically-aligned carbon nanotubes films grown on Ti in a
microwave plasma reactor. The morphology and the crystalline
structure of electrodeposited material were evaluated by scanning
electron microscopy and X-ray diffraction, respectively.
Thesamples presented difratograms containing peaks related both to
zinc oxide and hidrated zinc hydroxinitrate, The hydrated zinc
hydroxinitrate phase was transformed in zinc oxide only by thermal
annealing at temperatures slightly higher than 200oC. Differences
on the nanoparticles morphology (sferulites or nanosheets) were
observed varying the electrodeposition potencial or by using (or
not) of magnetic stirring.",
conference-location = "S{\~a}o Jos{\'e} dos Campos",
conference-year = "30 e 31 de julho de 2013",
copyholder = "SID/SCD",
language = "pt",
ibi = "8JMKD3MGP7W/3EPHJH5",
url = "http://urlib.net/ibi/8JMKD3MGP7W/3EPHJH5",
targetfile = "Pianassola_desenvolvimento.pdf",
urlaccessdate = "15 jun. 2024"
}