@InProceedings{BarbosaCoraLobo:2013:EsPaTe,
author = "Barbosa, Michelle Chizzolini and Corat, Evaldo Jos{\'e} and Lobo,
Anderson de Oliveira",
affiliation = "{} and {Instituto Nacional de Pesquisas Espaciais (INPE)} and
{Universidade do Vale do Para{\'{\i}}ba (UNIVAP)}",
title = "Estudo de par{\^a}metros termodin{\^a}micos na
eletrodeposi{\c{c}}{\~a}o de hidroxiapatita em nanotubos de
carbono verticalmente alinhados / Direct hydroxyapatite
electrodeposition on superhydrophilic vertically aligned carbon
nanotube films",
booktitle = "Anais...",
year = "2013",
organization = "Semin{\'a}rio de Inicia{\c{c}}{\~a}o Cient{\'{\i}}fica do
INPE (SICINPE).",
publisher = "INPE",
address = "S{\~a}o Jos{\'e} dos Campos",
note = "{Bolsa PIBIC/INPE/CNPq}",
keywords = "par{\^a}metros termodin{\^a}micos, eletrodeposi{\c{c}}{\~a}o,
nanotubos de carbono.",
abstract = "Na medicina regenerativa, nanotubos de carbono verticalmente
alinhados (VACNT), s{\~a}o de grande interesse. Moldes induzidos
a base de nanohidroxiapatita (HAp) tamb{\'e}m s{\~a}o de grande
interesse na medicina {\'o}sseo-regenerativa. Assim uma
combina{\c{c}}{\~a}o de ambas torna-se muito atraente para
aplica{\c{c}}{\~o}es de regenera{\c{c}}{\~a}o {\'o}ssea. Os
filmes de VACNTs foram produzidos utilizando um reator de plasma
de microondas a 2.45GHz sobre substratos de Ti (10x10x1mm).
Obteve-se a superhidrofilicidade dos VACNTs atrav{\'e}s da
funcionaliza{\c{c}}{\~a}o utilizando plasma de O2 com um reator
de plasma DC-Pulsado, tornando-os superhidrof{\'{\i}}licos
(VACNT-O2). A produ{\c{c}}{\~a}o de nanocomp{\'o}sitos de
HAp/VACNT-O2 foi realizada por eletrodeposi{\c{c}}{\~a}o de
cristais de HAp sobre os filmes de VACNT-O2. Os resultados mostram
que um grupo funcional carbox{\'{\i}}lico ligado ao VACNT-O2
ap{\'o}s a funcionaliza{\c{c}}{\~a}o a plasma foram essenciais
para a acelera{\c{c}}{\~a}o da forma{\c{c}}{\~a}o de OH- e
consequente deposi{\c{c}}{\~a}o dos cristais de HAp. O efeito da
temperatura foi essencial para acelerar o processo de
produ{\c{c}}{\~a}o da HA sobre os VACNT-O2 com homogeneidade e
cristalinidade. Tais resultados apresentaram-se como atrativos
visando a aplicabilidade dos nanocomp{\'o}sitos de HAp/VACNT-O2
para a regenera{\c{c}}{\~a}o {\'o}ssea. ABSTRACT: Vertically
aligned multiwalled carbonnanotubes (VACNT) is of particular
interest in regenerative medicine. Template-induced
nanohydroxyapatite (HAp) has broad prospects in applied fields of
bone regenerative medicine. Thus, it becomes very attractive a
combination these two excellent materials to bone tissue
engineering applications. VACNT films were produced as a thin
film, using a microwave plasma chamberat 2.45GHz on Ti substrates
(10mmx10mmx1mm). Superhydrophilic VACNT (VACNT-O2) films were
obtained by thein corporation of oxygen-containing groups using a
pulsed-direct current plasma reactor with pure oxygen. The
fabrication of HAp/VACNT-O2 nanocomposites was performed with a
direct electrodeposition of thethin HAp films on the VACNT-O2
films. Results shows that the carboxylic functional groups
directly attached on VACNT-O2 tips after oxygen plasma treat ment
were essential for the acceleration of the OH- formation and the
deposition of plate-like HAp crystals. The temperature effect was
essential to accelerate the production process of the HAp crystals
on VACNT-O2with homogeneity and cristallinity. These findings were
very attractive for application of these new HAp/VACNT-O2
nanocomposites to bone tissue regeneration.",
conference-location = "S{\~a}o Jos{\'e} dos Campos",
conference-year = "30 e 31 de julho de 2013",
copyholder = "SID/SCD",
language = "pt",
ibi = "8JMKD3MGP7W/3EPJ29B",
url = "http://urlib.net/ibi/8JMKD3MGP7W/3EPJ29B",
targetfile = "Barbosa_estudo.pdf",
urlaccessdate = "18 jun. 2024"
}