title = "Ensaios de compress{\~a}o e caracteriza{\c{c}}{\~a}o estrutural
de ligas Ti-7,5Si-22,5B produzidas por metalurgia do p{\'o} e 3IP
/ Compression tests and structural characterization of
Ti-7.5Si-22.5B alloys produced by powder metallurgy and PIII",
booktitle = "Anais...",
year = "2013",
organization = "Semin{\'a}rio de Inicia{\c{c}}{\~a}o Cient{\'{\i}}fica do
INPE (SICINPE).",
publisher = "INPE",
address = "S{\~a}o Jos{\'e} dos Campos",
note = "{Bolsa PIBIC/INPE/CNPq}",
keywords = "moagem de alta energia, implanta{\c{c}}{\~a}o i{\^o}nica por
imers{\~a}o em plasma, resist{\^e}ncia {\`a} compress{\~a}o,
high energy ball milling, plasma immersion ion implantation,
compression strength.",
abstract = "As ligas de tit{\^a}nio t{\^e}m atra{\'{\i}}do grande
interesse tecnol{\'o}gico, uma vez que possuem boas propriedades
mec{\^a}nicas e excelente resist{\^e}ncia {\`a} corros{\~a}o.
O presente trabalho trata do estudo de propriedades
f{\'{\i}}sico-qu{\'{\i}}micas da liga Ti-7,5Si-22,5B,
preparada por moagem de alta energia, sinteriza{\c{c}}{\~a}o e
implanta{\c{c}}{\~a}o i{\^o}nica por imers{\~a}o em plasma de
nitrog{\^e}nio (3IP-N). As caracteriza{\c{c}}{\~o}es foram
realizadas utilizando Microscopia Eletr{\^o}nica de Varredura
(MEV), Difra{\c{c}}{\~a}o de Raios X (DRX), perfilometria
{\'o}ptica e ensaios de compress{\~a}o. Os resultados de DRX e
MEV da liga Ti-7,5Si-22,5B sem tratamento evidenciam que a moagem
de alta energia combinada com a prensagem a quente produz as
seguintes fases: Ti alfa, Ti6Si2B, Ti3Si, Ti5Si3 e TiB. A liga
Ti-6Al-4V foi utilizada como meio de compara{\c{c}}{\~a}o nos
ensaios de compress{\~a}o. Ap{\'o}s o tratamento superficial por
plasma, as an{\'a}lises de DRX evidenciaram a presen{\c{c}}a de
nitretos na liga Ti-6Al-4V, o que n{\~a}o p{\^o}de ser
verificado na liga Ti-7,5Si-22,5B por essa t{\'e}cnica de
caracteriza{\c{c}}{\~a}o. Os picos de difra{\c{c}}{\~a}o dos
nitretos nesta liga s{\~a}o sutis, assim como os observados na
liga Ti-6Al-4V. Pela an{\'a}lise por EDS (Energy Dispersive
Spectroscopy) {\'e} poss{\'{\i}}vel identificar a
presen{\c{c}}a de nitrog{\^e}nio em ambas ligas. A liga
Ti-7,5Si-22,5B foi obtida com alta densifica{\c{c}}{\~a}o e sua
for{\c{c}}a de ruptura da atingiu cerca de 1875 MPa; que ocorreu
devido {\`a} porosidade e escorregamento dos planos cristalinos.
As fractografias da liga Ti-7,5Si-22,5B obtidas por MEV revelam
que as rupturas ocorreram por fraturas transgranulares,
intergranulares e por porosidade, o que depende do tempo de
moagem. ABSTRACT: Titanium alloys have attracted high
technological interest, since they have good mechanical properties
and excellent corrosion resistance. The present work treats on
study of physicochemical properties of the Ti-7.5Si-22.5B alloy,
prepared by high energy ball milling, sintering and plasma
immersion ion implantation (PIII). Characterizations were
performed using scanning electron microscopy (SEM), X-ray
Diffraction (XRD), optical profilometry and compression tests. XRD
and SEM results of untreated Ti-7.5Si-22.5B alloy show that high
energy ball milling combined with hot pressing produces the
following phases: Ti alpha, Ti6Si2B, Ti3Si, Ti5Si3 and TiB.
Ti-6Al-4V was used as a comparison in the compression tests. After
plasma surface treatment, XRD analysis showed nitrides in
Ti-6Al-4V, which is not verified in the Ti-7.5Si-22.5B alloy
through this characterization technique. XRD peaks of nitrides in
this alloy are subtle, like those observed in Ti-6Al-4V. Through
EDS (Energy Dispersive Spectroscopy) it is possible to identify
the presence of nitrogen in both alloys. The Ti-7.5Si-22.B alloy
was obtained with high densification and its rupture strength
reached around 2000 MPa, which occurred due to porosity and slip
of crystal planes. Fractographies of the Ti-7.5Si-22.5B alloy
showed that ruptures occurred through transgranular and
intergranular fractures and porosity, which depends on the milling
time.",
conference-location = "S{\~a}o Jos{\'e} dos Campos",
conference-year = "30 e 31 de julho de 2013",
copyholder = "SID/SCD",
language = "pt",
ibi = "8JMKD3MGP7W/3EP83M8",
url = "http://urlib.net/ibi/8JMKD3MGP7W/3EP83M8",
targetfile = "Silva_ensaios.pdf",
urlaccessdate = "02 maio 2024"
}