@MastersThesis{Silva:2020:PrCaCa,
               author = "Silva, Raissa Samira Rocha da",
                title = "Processamento e caracteriza{\c{c}}{\~a}o do carbono 
                         v{\'{\i}}treo reticulado modificado com grafite expandida",
               school = "Instituto Nacional de Pesquisas Espaciais (INPE)",
                 year = "2020",
              address = "S{\~a}o Jos{\'e} dos Campos",
                month = "2020-02-21",
             keywords = "resina furfur{\'{\i}}lica, CVR, grafite expandida, eletrodos, 
                         poly (furfuryl alcohol), carbon foam composites, expanded 
                         graphite, electrodes.",
             abstract = "Comp{\'o}sitos polim{\'e}ricos contendo estruturas de grafite 
                         como agente modificador s{\~a}o processados com sucesso, exibindo 
                         caracter{\'{\i}}sticas atraentes para uma variedade de 
                         aplica{\c{c}}{\~o}es. As espumas de carbono derivadas do 
                         precursor polim{\'e}rico, como o carbono v{\'{\i}}treo 
                         reticulado (CVR), s{\~a}o muito utilizadas como eletrodos, mas 
                         apresentam grande fragilidade estrutural. Sendo assim, {\'e} de 
                         grande interesse o uso de um refor{\c{c}}o, n{\~a}o apenas para 
                         melhorar as propriedades mec{\^a}nicas, mas para fins 
                         multifuncionais. Considerando as vantagens oferecidas pelas 
                         diferentes estruturas de grafite modificada adicionadas aos 
                         comp{\'o}sitos polim{\'e}ricos, incluindo baixo pre{\c{c}}o, 
                         facilidade de dispers{\~a}o, boa estabilidade t{\'e}rmica, 
                         condutividade el{\'e}trica e propriedades mec{\^a}nicas, neste 
                         trabalho a grafite expandida (GE) foi escolhida como aditivo para 
                         o processamento de espumas de carbono modificadas. A resina 
                         furfur{\'{\i}}lica foi sintetizada a partir do {\'a}lcool 
                         furfur{\'{\i}}lico e utilizada como matriz precursora do CVR, 
                         sendo acrescida de diferentes porcentagens em massa de GE. A 
                         avalia{\c{c}}{\~a}o da resina com GE por viscosimetria e 
                         calorimetria explorat{\'o}ria diferencial mostrou que o GE 
                         auxiliou na forma{\c{c}}{\~a}o das liga{\c{c}}{\~o}es cruzadas 
                         e reduziu a temperatura de in{\'{\i}}cio e final de cura devido 
                         a presen{\c{c}}a de grupos funcionais na sua superf{\'{\i}}cie 
                         que atuam como catalisador. A adi{\c{c}}{\~a}o de at{\'e} 1% em 
                         massa do GE manteve uma boa fluidez da resina o que garantiu uma 
                         boa impregna{\c{c}}{\~a}o das espumas de poliuretano usadas como 
                         molde para o processamento do CVR modificado. Os resultados da 
                         caracteriza{\c{c}}{\~a}o do CVR mostraram que a presen{\c{c}}a 
                         de GE contribuiu para melhorar a cristalinidade, resist{\^e}ncia 
                         {\`a} compress{\~a}o, al{\'e}m de rea{\c{c}}{\~o}es de 
                         transfer{\^e}ncia de carga e {\'a}rea superficial 
                         eletroqu{\'{\i}}mica espec{\'{\i}}fica. Portanto, a 
                         efic{\'a}cia do comp{\'o}sito de carbono resultante foi 
                         atribu{\'{\i}}da principalmente {\`a} boa intera{\c{c}}{\~a}o 
                         entre GE e matriz de carbono. ABSTRACT: Polymer composites 
                         containing graphite structures as a modifying agent are 
                         successfully processed, exhibiting attractive characteristics for 
                         a variety of applications. Carbon foams derived from the polymeric 
                         precursor, such as reticulated vitreous carbon (RVC), are widely 
                         used as electrodes but have great structural fragility. In this 
                         sense, the use of reinforcement is of great interest, not only to 
                         improve mechanical properties but for multifunctional purposes. 
                         Considering the advantages offered by the different modified 
                         graphite structures added to the polymer composites, including low 
                         price, ease of dispersion, good thermal stability, electrical 
                         conductivity, and mechanical properties, in this work the expanded 
                         graphite (EG) was chosen as an additive for the processing of 
                         modified carbon foams. Poly(furfuryl alcohol) was synthesized from 
                         furfuryl alcohol and used as a precursor matrix of RVC with the 
                         addition of different EG mass percentages. The evaluation of the 
                         resin with EG by viscosimetry and differential scanning 
                         calorimetry showed that EG helped in the formation of cross-links 
                         and reduced the onset and endset temperature due to the presence 
                         of functional groups on its surface that acted as a catalyst. The 
                         addition of up to 1% by weight of EG maintained a good fluidity of 
                         the resin, which ensured a good impregnation of the polyurethane 
                         foams used as a template for the EG modified RVC processing. RVC 
                         characterizations showed that the EG presence contributed to 
                         improve its crystallinity, compressive strength, charge transfer 
                         reactions, and specific electrochemical surface area. Therefore, 
                         the effectiveness of the resulting carbon composite was mainly 
                         attributed to the good interaction between EG and carbon matrix.",
            committee = "Ferreira, Neiden{\^e}i Gomes (presidente/orientadora) and Oishi, 
                         Silvia Sizuka (orientadora) and Martins, Gislene Valdete and 
                         Botelho, Edson Cocchieri",
         englishtitle = "Processing and characterization of modified reticulated vitreous 
                         carbon with expanded graphite",
             language = "pt",
                pages = "77",
                  ibi = "8JMKD3MGP3W34R/3USL728",
                  url = "http://urlib.net/ibi/8JMKD3MGP3W34R/3USL728",
           targetfile = "publicacao.pdf",
        urlaccessdate = "18 abr. 2024"
}