@MastersThesis{Horban:2021:CaElTe,
               author = "Horban, Marco Aurelio",
                title = "Caracteriza{\c{c}}{\~a}o eletroqu{\'{\i}}mica e 
                         termo-{\'o}ptica do alum{\'{\i}}nio anodizado negro",
               school = "Instituto Nacional de Pesquisas Espaciais (INPE)",
                 year = "2021",
              address = "S{\~a}o Jos{\'e} dos Campos",
                month = "2020-09-23",
             keywords = "anodiza{\c{c}}{\~a}o, alum{\'{\i}}nio, corros{\~a}o, 
                         propriedades termo-{\'o}pticas, anodizing, aluminum, corrosion, 
                         thermo-optical properties.",
             abstract = "A anodiza{\c{c}}{\~a}o de ligas de alum{\'{\i}}nio {\'e} 
                         amplamente utilizada pela ind{\'u}stria aeroespacial devido a 
                         suas caracter{\'{\i}}sticas anticorrosivas. Al{\'e}m disso, o 
                         alum{\'{\i}}nio anodizado pode ser colorido a fim de prover ao 
                         material propriedades termo-{\'o}pticas espec{\'{\i}}ficas, 
                         tornando-o apto para a aplica{\c{c}}{\~a}o no controle 
                         t{\'e}rmico passivo de sat{\'e}lites. No entanto, a 
                         influ{\^e}ncia das vari{\'a}veis de processo na 
                         forma{\c{c}}{\~a}o da camada de {\'o}xido an{\'o}dico ainda 
                         n{\~a}o {\'e} completamente compreendida. Dessa forma, este 
                         trabalho se prop{\^o}s a estudar o efeito da 
                         concentra{\c{c}}{\~a}o de H2SO4 no eletr{\'o}lito e o tempo de 
                         anodiza{\c{c}}{\~a}o sobre a resist{\^e}ncia {\`a} 
                         corros{\~a}o do alum{\'{\i}}nio anodizado n{\~a}o colorido. 
                         Adicionalmente, foi investigado o impacto da 
                         concentra{\c{c}}{\~a}o do eletr{\'o}lito nas propriedades 
                         termo-{\'o}pticas e qu{\'{\i}}micas em amostras de 
                         alum{\'{\i}}nio anodizado negro. Para isso, amostras de 
                         alum{\'{\i}}nio de liga 2024, 6061 e 7075 foram anodizadas e 
                         caracterizadas fazendo uso de microscopia eletr{\^o}nica de 
                         varredura, espectroscopia de raios X por dispers{\~a}o de 
                         energia, polariza{\c{c}}{\~a}o potenciodin{\^a}mica e 
                         espectroscopia de imped{\^a}ncia eletroqu{\'{\i}}mica. Ademais, 
                         as amostras submetidas ao processo de colora{\c{c}}{\~a}o 
                         passaram por caracteriza{\c{c}}{\~o}es adicionais utilizando 
                         perfilometria {\'o}ptica e espectrofotometria. Foi observada uma 
                         tend{\^e}ncia de aumento de espessura das camadas an{\'o}dicas 
                         proporcional ao tempo de anodiza{\c{c}}{\~a}o. Paralelamente, as 
                         amostras anodizadas com menores concentra{\c{c}}{\~o}es de H2SO4 
                         apresentaram melhores resultados de resist{\^e}ncia {\`a} 
                         corros{\~a}o. A liga 7075 n{\~a}o apresentou 
                         colora{\c{c}}{\~a}o negra para nenhuma condi{\c{c}}{\~a}o de 
                         eletr{\'o}lito utilizada. Enquanto a liga 2024 apresentou 
                         melhoria das propriedades termo{\'o}pticas ao se utilizar 
                         eletr{\'o}lito com maiores concentra{\c{c}}{\~o}es de H2SO4, a 
                         liga 6061 teve suas propriedades termo-{\'o}pticas beneficiadas 
                         com o uso de eletr{\'o}litos menos concentrados. ABSTRACT: The 
                         anodizing of aluminum alloys is widely utilized by the aerospace 
                         industry due to its anticorrosive characteristics. Besides, the 
                         anodized aluminum can be colored in order to provide specific 
                         thermo-optical properties to the material, making it suitable to 
                         application in the passive thermal control of satellites. However, 
                         the influence of variables in the process of anodic layer 
                         formation is not completely understood. Thus, this work proposed 
                         the study of the effect of H2SO4 concentration in the electrolyte 
                         and the anodizing time on the corrosion resistance of non-colored 
                         anodized aluminum. Additionally, the impact of electrolyte 
                         concentration on thermo-optical and chemical properties of black 
                         anodized aluminum samples was investigated. For this purpose, 
                         2024, 6061 and 7075 aluminum alloys samples were anodized and 
                         characterized by scanning electron microscopy, energy-dispersive 
                         X-ray spectroscopy, potentiodynamic polarization and 
                         electrochemical impedance spectroscopy. Furthermore, samples 
                         subjected to the coloring process went through additional 
                         characterizations with optical profilometry and spectrophotometry. 
                         A tendency of rise in anodic layer thickness proportional to 
                         anodizing time was observed. In parallel, samples anodized with 
                         lower H2SO4 concentration presented better results for corrosion 
                         resistance. The 7075 alloy did not achieve a black coloring with 
                         any electrolyte condition utilized. While the 2024 alloy presented 
                         an improvement in its thermo-optical properties when electrolytes 
                         with higher H2SO4 concentration were used, the 6061 alloy had 
                         their thermo-optical properties favored by the use of less 
                         concentrated electrolytes.",
            committee = "Mello, Carina Barros (presidente) and Savonov, Graziela da Silva 
                         (orientadora) and May, Jos{\'e} Eduardo (orientador) and Berni, 
                         Luiz Angelo and Gon{\c{c}}alves, Emerson Sarmento and Oliveira, 
                         Rog{\'e}rio De Moraes",
         englishtitle = "Electrochemical and thermo-optical characterization of black 
                         anodized aluminum",