@TechReport{NogueiraLopeBald:2020:CaPrEl,
author = "Nogueira, Aline de Oliveira Sant'Anna and Lopes, Braulio Haruo
Kondo and Baldan, Maur{\'{\i}}cio Ribeiro",
title = "Caracteriza{\c{c}}{\~a}o das propriedades eletromagn{\'e}ticas
de comp{\'o}sitos h{\'{\i}}bridos a base de aditivos
el{\'e}tricos e magn{\'e}ticos dispersos em matrizes
diel{\'e}tricas na faixa de frequ{\^e}ncia de micro-ondas
referente a banda X",
institution = "Instituto Nacional de Pesquisas Espaciais",
year = "2020",
type = "RPQ",
address = "S{\~a}o Jos{\'e} dos Campos",
note = "{Bolsa PIBIC/INPE/CNPq.}",
keywords = "Materiais absorvedores de radia{\c{c}}{\~a}o
eletromagn{\'e}tica, banda X, comp{\'o}sitos polim{\'e}ricos,
grafite, electromagnetic radiation absorbing materials, band X,
polymeric composites, graphite.",
abstract = "O desenvolvimento de materiais com boa capacidade de
absor{\c{c}}{\~a}o de radia{\c{c}}{\~o}es
eletromagn{\'e}ticas {\'e} muito importante para setores como
civil, militar e aeroespacial, devido {\`a} grande quantidade de
radia{\c{c}}{\~a}o na qual alguns dispositivos s{\~a}o
expostos. Os comp{\'o}sitos a base de aditivos magn{\'e}ticos e
el{\'e}tricos dispersos em matrizes de pol{\'{\i}}meros
diel{\'e}tricos que al{\'e}m de diminuir a energia das
radia{\c{c}}{\~o}es, possuem baixo peso e boa processabilidade.
Estes materiais s{\~a}o chamados de materiais absorvedores de
radia{\c{c}}{\~a}o eletromagn{\'e}tica (MARE) e podem ser
constitu{\'{\i}}dos a base de carbono, ferrita, negro de fumo,
{\'o}xido de grafeno, fibras de carbono e pol{\'{\i}}mero,
unidos a algum filtro magn{\'e}tico e diel{\'e}trico. O presente
trabalho tem como objetivo o desenvolvimento de comp{\'o}sitos
h{\'{\i}}bridos, a base de aditivos magn{\'e}ticos e
el{\'e}tricos, dispersos em uma matriz de silicone branco. Foram
produzidas amostras com particulados de ferrita mangan{\^e}s e
zinco (FeMnZn) com grafite (G) e amostras com particulados de
ferro carbonila (FC) com grafite. A propor{\c{c}}{\~a}o do
aditivo el{\'e}trico (grafite) foi variada, utilizando
porcentagens de 1, 5, 10 e 15% em rela{\c{c}}{\~a}o a quantidade
em massa de silicone branco. J{\'a} os aditivos magn{\'e}ticos
(FeMnZn e FC) foram determinadas uma concentra{\c{c}}{\~a}o fixa
de 70 % em peso dos particulados em todas as amostras. As
dimens{\~o}es das amostras foram de 10,2 x 22,9 mm e com
espessura de 2 mm. A caracteriza{\c{c}}{\~a}o
eletromagn{\'e}tica foi realizada atrav{\'e}s de um Analisador
de Rede Vetorial e guia de onda retangular WR90, e a faixa de
frequ{\^e}ncia analisada foi de 8,2 a 12,4 GHz, referente a banda
X, utilizada em setores de telecomunica{\c{c}}{\~o}es,
dispositivos de sat{\'e}lites e radares militares. Os resultados
obtidos a partir do ensaio da refletividade apresentaram altos
valores (>90%) de absor{\c{c}}{\~a}o da radia{\c{c}}{\~a}o
eletromagn{\'e}tica e houve um aumento da capacidade de armazenar
energia dos comp{\'o}sitos sem altera{\c{c}}{\~a}o no seu
comportamento eletromagn{\'e}tico de forma macrosc{\'o}pica.
ABSTRACT: The development of materials with good absorption
capacity of electromagnetic radiation is very important for
sectors such as civil, military and aerospace, due to the large
amount of radiation in which some devices are exposed. Composites
based on magnetic and electrical additives dispersed in dielectric
polymer matrices that, in addition to reducing the energy of
radiation, have low weight and good processability. These
materials are called electromagnetic radiation absorbing materials
(MARE) and can be constituted based on carbon, ferrite, carbon
black, graphene oxide, carbon fibers and polymer, joined to some
magnetic and dielectric filter. The present work aims to develop
hybrid composites, based on magnetic and electrical additives,
dispersed in a white silicone matrix. Samples were produced with
manganese ferrite and zinc particulates (FeMnZn) with graphite (G)
and samples with carbonyl iron particulates (FC) with graphite.
The proportion of the electric additive (graphite) was varied,
using percentages of 1, 5, 10 and 15% in relation to the mass
quantity of white silicone. Magnetic additives (FeMnZn and FC)
were determined at a fixed concentration of 70 % by weight of
particulates in all samples. The sample dimensions were 10.2 x
22.9 mm and with a thickness of 2 mm. The electromagnetic
characterization was performed through a Vector Network Analyzer
and rectangular waveguide WR90, and the frequency range analyzed
was 8.2 to 12.4 GHz, referring to the X-band, used in
telecommunications sectors, satellite devices and military radars.
The results obtained from the reflectivity assay showed high
values (>90%) electromagnetic radiation absorption and there was
an increase in the ability to store energy from composites without
alteration in their electromagnetic behavior in a macroscopic
manner.",
affiliation = "Instituto Federal de Ci{\^e}ncia, Educa{\c{c}}{\~a}o e
Tecnologia and {Instituto Nacional de Pesquisas Espaciais (INPE)}
and {Instituto Nacional de Pesquisas Espaciais (INPE)}",
language = "pt",
pages = "48",
ibi = "8JMKD3MGP3W34R/43SF79L",
url = "http://urlib.net/ibi/8JMKD3MGP3W34R/43SF79L",
targetfile = "PIBIC - Aline de Oliveira Sant'Anna Nogueira - Relat{\'o}rio
Final..pdf",
urlaccessdate = "18 abr. 2024"
}