| 1. Identificação | |
| Tipo de Referência | Artigo em Revista Científica (Journal Article) |
| Site | mtc-m21b.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | 8JMKD3MGP5W34M/3HE6FL9 |
| Repositório | sid.inpe.br/mtc-m21b/2014/11.19.00.01.28 (acesso restrito) |
| Última Atualização | 2015:02.10.14.22.09 (UTC) administrator |
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2014/11.19.00.01.29 |
| Última Atualização dos Metadados | 2018:06.04.03.04.34 (UTC) administrator |
| DOI | 10.1016/j.apsusc.2014.05.047 |
| ISSN | 0169-4332 |
| Rótulo | scopus 2014-11 OliveiraOlivReisCarr:2014:EfNiHi |
| Chave de Citação | OliveiraOlivReisCarr:2014:EfNiHi |
| Título | Effect of nitrogen high temperature plasma based ion implantation on the creep behavior of Ti-6Al-4V alloy  |
| Ano | 2014 |
| Data de Acesso | 26 abr. 2024 |
| Tipo de Trabalho | journal article |
| Tipo Secundário | PRE PI |
| Número de Arquivos | 1 |
| Tamanho | 2011 KiB |
| 2. Contextualização | |
| Autor | 1 Oliveira, Aline Capella de 2 Oliveira, Rogerio de Moraes 3 Reis, D. A. P. 4 Carreri, Felipe de Campos |
| Identificador de Curriculo | 1 2 8JMKD3MGP5W/3C9JJ6L |
| Grupo | 1 LAP-CTE-INPE-MCTI-GOV-BR 2 LAP-CTE-INPE-MCTI-GOV-BR 3 4 LAP-CTE-INPE-MCTI-GOV-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Universidade Federal de São Paulo (UNIFESP) 4 Instituto Nacional de Pesquisas Espaciais (INPE) |
| Endereço de e-Mail do Autor | 1 alinecapella@gmail.com |
| Endereço de e-Mail | marcelo.pazos@inpe.br |
| Revista | Applied Surface Science |
| Volume | 311 |
| Páginas | 239-244 |
| Nota Secundária | A1_ENGENHARIAS_II A1_ENGENHARIAS_I A1_INTERDISCIPLINAR A2_ENGENHARIAS_III A2_CIÊNCIAS_AGRÁRIAS_I A2_MATERIAIS A2_SAÚDE_COLETIVA B1_GEOCIÊNCIAS B1_ODONTOLOGIA B1_QUÍMICA B1_CIÊNCIAS_BIOLÓGICAS_I B1_ENGENHARIAS_IV B1_MATEMÁTICA_/_PROBABILIDADE_E B1_MEDICINA_II B1_MEDICINA_III B1_FARMÁCIA B1_BIOTECNOLOGIA B2_ENSINO B2_ASTRONOMIA_/_FÍSICA B2_CIÊNCIAS_BIOLÓGICAS_II C_BIODIVERSIDADE |
| Histórico (UTC) | 2018-06-04 03:04:34 :: administrator -> marcelo.pazos@inpe.br :: 2014 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Aluminum Ion implantation Nitrogen Titanium alloys Constant load creep tests Creep behaviors High-temperature plasmas Micro-structural characterization Plasma-based ion implantation Simultaneous formation Steady state creep rate Ti-6Al-4V alloy Creep |
| Resumo | Nitrogen high temperature plasma based ion implantation (HTPBII) performed on Ti-6Al-4V significantly improved the creep behavior of the alloy. Treatments were performed for 1 h at a working pressure of 4 mbar and negative high voltage pulses of 7.5 kV, 30 ¼s and 500 Hz were applied on the specimens heated at 800 °C and 900 °C, respectively. Microstructural characterization of the treated samples revealed the formation of nitrided layers, with simultaneous formation of TiN and Ti2N. The most intense peaks of these compounds were obtained at higher treatment temperature, probably due to the diffusion of nitrogen into titanium. The presence of nitrides caused surface hardening up to three times higher in comparison with untreated alloy. Constant load creep tests were conducted on a standard creep machine in air atmosphere, at stress level of 319 MPa at 600 °C. Significant reductions of the steady-state creep rates (µ) were measured for martensitic Ti-6Al-4V treated by nitrogen HTPBII, reaching minimum creep rates of 0.0318 h-1 in comparison with 0.1938 h-1 for untreated sample. The improvement of the creep resistance seems to be associated with the formation of a thick nitrided layer, which acts as a barrier to oxygen diffusion into the material. In addition, the increase of the grain size generated by the heating of the substrate during the treatment can affect some creep mechanisms, leading to a significant reduction of µ. © 2014 Elsevier B.V. |
| Área | FISPLASMA |
| Arranjo | Effect of nitrogen... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| Idioma | en |
| Grupo de Usuários | administrator marcelo.pazos@inpe.br |
| Grupo de Leitores | administrator marcelo.pazos@inpe.br |
| Visibilidade | shown |
| Política de Arquivamento | denypublisher denyfinaldraft24 |
| Permissão de Leitura | deny from all and allow from 150.163 |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Vinculação | Trabalho não Vinculado à Tese/Dissertação |
| Repositório Espelho | iconet.com.br/banon/2006/11.26.21.31 |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
| Lista de Itens Citando | sid.inpe.br/mtc-m21/2012/07.13.14.59.24 2 sid.inpe.br/bibdigital/2013/09.25.21.49 1 |
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX; SCOPUS. |
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 |
| 6. Notas | |
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel format isbn lineage mark month nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject targetfile tertiarytype url |
| 7. Controle da descrição | |
| e-Mail (login) | marcelo.pazos@inpe.br |
| atualizar | |