| 1. Identity statement | |
| Reference Type | Journal Article |
| Site | mtc-m16b.sid.inpe.br |
| Holder Code | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identifier | 6qtX3pFwXQZGivnK2Y/S9iNq |
| Repository | sid.inpe.br/mtc-m17@80/2007/11.13.12.51 (restricted access) |
| Last Update | 2007:11.13.12.51.33 (UTC) administrator |
| Metadata Repository | sid.inpe.br/mtc-m17@80/2007/11.13.12.51.34 |
| Metadata Last Update | 2018:06.05.03.35.01 (UTC) administrator |
| Secondary Key | INPE-14899-PRE/9813 |
| ISSN | 0257-8972 |
| Citation Key | SilvaUedaSilvCoda:2007:CoBeTi |
| Title | Corrosion behavior of Ti-6Al-4V alloy treated by plasma immersion ion implantation process  |
| Year | 2007 |
| Month | Aug. |
| Access Date | 2024, Apr. 28 |
| Secondary Type | PRE PI |
| Number of Files | 1 |
| Size | 777 KiB |
| 2. Context | |
| Author | 1 Silva, Leide Lili Gonçalves da 2 Ueda, Mário 3 Silva, M. M. 4 Codaro, E. N. |
| Group | 1 LAP-INPE-MCT-BR 2 LAP-INPE-MCT-BR |
| Affiliation | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Department of Mechanical Engineering, Technological Institute of Aeronautics (ITA) 4 Faculdade de Engenharia de Guaratinguetá. Universidade Estadual Paulista (FEG.UNESP) |
| Author e-Mail Address | 1 leide@plasma.inpe.br |
| Journal | Surface and Coatings Technology |
| Volume | 201 |
| Number | 19/20 |
| Pages | 8136-8139 |
| History (UTC) | 2007-11-13 13:03:02 :: simone -> administrator :: 2008-06-29 02:36:49 :: administrator -> simone :: 2011-05-29 09:47:36 :: simone -> administrator :: 2012-10-23 23:58:43 :: administrator -> simone :: 2007 2013-02-20 15:20:02 :: simone -> administrator :: 2007 2018-06-05 03:35:01 :: administrator -> marciana :: 2007 |
| 3. Content and structure | |
| Is the master or a copy? | is the master |
| Content Stage | completed |
| Transferable | 1 |
| Content Type | External Contribution |
| Keywords | Ti-6Al-4V alloy plasma immersion ion implantation corrosion nitride layer TITANIUM RESISTANCE FILMS OXIDE |
| Abstract | Ti-6Al-4V alloy is one of the most frequently used Ti alloys with diverse applications in aerospace and biomedical areas due to its favorable mechanical properties, corrosion resistance and biocompatibility. Meanwhile, its surface can stiffer intense corrosion caused by wear processes due to its poor tribological properties. Thus in the present study, PIII processing of Ti-6Al-4V alloy was carried out to evaluate its corrosion resistance in 3.5% NaCl solution. Two different sets of Ti-6Al-4V samples were PIII treated, varying the plasma gases and the treatment time. The corrosion behavior is correlated with the surface morphology, and the nitrogen content. SEM micrographs of the untreated sample reveal a typical two-phase structure. PIII processing promotes surface sputtering and the surface morphology is completely different for samples treated with N-2/H-2 mixture and N-2 only. The highest penetration of nitrogen (similar to 88 nm), corresponding to 33% of N-2 was obtained for the sample treated with N-2/H-2 mixture for 1:30 h. The corrosion behavior of the samples was investigated by a potentiodynamic polarization method. A large passive region of the polarization curves (similar to 1.5 V), associated with the formation of a protective film, was observed for all samples. The passive current density (similar to 3 x 10(-6) A cm(-2)) of the PIII-treated Ti-6Al-4V samples is about 10 times higher than for the untreated sample. This current value is still rather low and maintains good corrosion resistance. The anodic branches of the polarization curves for all treated Ti-6Al-4V samples demonstrate also that the oxide films break down at approximately 1.6 V, forming an active region. Although the sample treated by N-2/H-2 mixture for 1.30 It has thicker nitrogen enriched layer, better corrosion resistance is obtained for the PIII process performed with N, gas only. |
| Area | FISPLASMA |
| Arrangement | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Corrosion behavior of... |
| doc Directory Content | access |
| source Directory Content | there are no files |
| agreement Directory Content | there are no files |
| 4. Conditions of access and use | |
| Language | en |
| Target File | corrosion beharvior of ti 6al 4v alloy.pdf |
| User Group | administrator simone |
| Visibility | shown |
| Copy Holder | SID/SCD |
| Archiving Policy | denypublisher denyfinaldraft24 |
| Read Permission | deny from all and allow from 150.163 |
| 5. Allied materials | |
| Next Higher Units | 8JMKD3MGPCW/3ET2RFS |
| Dissemination | WEBSCI; PORTALCAPES. |
| Host Collection | lcp.inpe.br/ignes/2004/02.12.18.39 cptec.inpe.br/walmeida/2003/04.25.17.12 |
| 6. Notes | |
| Empty Fields | alternatejournal archivist callnumber copyright creatorhistory descriptionlevel documentstage doi e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project readergroup resumeid rightsholder schedulinginformation secondarydate secondarymark session shorttitle sponsor subject tertiarymark tertiarytype typeofwork url versiontype |
| 7. Description control | |
| e-Mail (login) | marciana |
| update | |